Silane coupling agent인 MPS 농도별처리에 따른 열중합 레진과 자가중합 레진 간의 전단결합강도

• Published in: 한국콘텐츠학회 논문지, 15(2) Vol. 15; no. 2; pp. 344 - 351
• Main Authors: 최에스더(Esther Choi), 권은자(Eun-Ja Kwon)
• Format: Journal Article
• Language: Korean
• Published: 한국콘텐츠학회 2015
• Subjects: 학제간연구; Silane Coupling Agent; 자가중합레진; 실란; Shear Bond Strength; Self Curing Resins; Denture Base Resin; 열중합 레진; 전단결합강도
• ISSN: 1598-4877; 2508-6723
• DOI: 10.5392/JKCA.2015.15.02.344

The purpose of this study was to evaluate the effect of the surface treatment of widely used in dental of silane coupling agent concentration on the shear bond strength of denture base resin and self curing resins. Denture base resin surface was treated with silane coupling agent concentration, after self curing resins were injected shear bond strength was measured. The results of silane coupling agent(MPS) concentration on the shear bond strength of Vertex self curing resin showed that the value of 5%, 7% groups were higher than that of other group(P<0.05). Silane coupling agent concentration on the shear bond strength of Kooliner resin showed that the value of 5% was highest(P<0.05). Therefore, we could conclude 5% MPS to strengthen effectively the shear bonding property of denture base resin and self curing resins of this study. 본 논문은 치과에서 많이 사용되고 있는 silane coupling agent로 표면 처리한 의치상 레진과 자가중합 레진 간의 전단 결합력에 미치는 영향에 대해 알아보고자 하였다. 의치상 레진에 silane coupling agent 농도별 표면 처리 후 자가중합레진을 주입하여 전단결합강도를 측정하였다. Silane coupling agent(MPS)의 농도별 표면 처리에 따른 의치상 레진과 자가중합레진 간의 전단결합강도에서는 Vertex self curing resin에서 5%, 7%에서 유의적으로 높게 나타났고(P<0.05), Kooliner에서는 5%에서 유의적으로 가장 높게 나타났다(P<0.05). 따라서 의치상 레진과 자가중합레진 사이에 MPS 5%를 이용한 표면처리가 전단결합강도에 효과적으로 영향을 미치는 것이라 사료된다.