Study on the Properties and Mechanism of Recycled Aggregate/Asphalt Interface Modified by Silane Coupling Agent

• Published in: Applied sciences Vol. 13; no. 18; p. 10343
• Main Authors: Zhou, Jiawang, Hu, Kui, Gao, Junfeng, Chen, Yujing, Yang, Qilin, Du, Xiaotong
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01.09.2023
• Subjects: Aggregates; Air quality management; Asphalt pavements; Cement hydration; Chemical bonds; China; Concrete; Emissions (Pollution); Energy; Energy conservation; Ethanol; High temperature; Hydrogen; interface reinforcement mechanism; molecular dynamic; Molecular dynamics; RCA/asphalt interface; recycled concrete aggregates; Research methodology; Silane; silane coupling agent; Sludge; Water damage; China
• ISSN: 2076-3417; 2076-3417
• DOI: 10.3390/app131810343

The use of recycled concrete aggregates (RCA) instead of natural aggregates in hot-mix asphalt mixtures is one of the ways to achieve energy savings and reduce carbon emissions in road engineering. However, the cement mortar on the surface of RCA adversely affects the adhesion properties between asphalt and aggregates, leading to a reduction in the performance characteristics of asphalt mixtures. In this study, a silane coupling agent (SCA) was employed to improve the adhesion properties of the RCA/asphalt interface. The enhancement mechanism of SCA on the RCA/asphalt interface was investigated from multiple perspectives, including macroscopic properties, interfacial microstructure, and nanoscale interfacial interactions. Firstly, the adhesion behavior and tensile strength of the interface between RCA and asphalt were determined through a boiling water test and direct tensile test, both before and after SCA modification. Secondly, scanning electron microscopy (SEM) was employed to observe the surface microstructure of RCA and the microstructure of the RCA/asphalt interface. Finally, the main component of mortar, calcium silicate hydrate (C-S-H), was taken as the research subject of investigation to examine the hydrogen bonding, interaction energy, and interface transition zone of the C-S-H/asphalt interface system using the molecular dynamics methodology. The results demonstrate a two-level enhancement in the adhesion performance of the interface at the macroscopic scale following SCA modification. The interface tensile strength increased by 72.2% and 119.7% under dry and wet conditions, respectively. At the microscopic scale, it was observed that the surface pores of RCA were repaired after SCA modification, resulting in a more tightly bonded interface between the RCA and asphalt. At the nanoscale, SCA modification reduces the hydrophilicity of the C-S-H surface, increases the interaction energy and water resistance of the C-S-H/asphalt interface, and enhances the weak interface transition zone between C-S-H and asphalt. This study provides a theoretical basis for using SCA to enhance the bond strength of the RCA/asphalt interface and lays the foundation for the application of RCA asphalt mixtures on highways.