Cyclic oxidation of high temperature materials : mechanisms, testing methods, characterisation and life time estimation : proceedings of an EFC Workshop, Frankfurt/Main, 1999

Saved in:
Bibliographic Details
Corporate Authors European Federation of Corrosion, Institute of Materials (Great Britain)
Other Authors Schütze, Michael, Quadakkers, W. J.
Format Electronic eBook
LanguageEnglish
Published London : Published for the European Federation of Corrosion by IOM Communications, 1999.
SeriesPublications (European Federation of Corrosion) ; no. 27.
Subjects
Materials at high temperatures > Congresses.
Oxidation > Congresses.
elektronické knihy
electronic books
Online AccessFull text
ISBN9781907625510
1907625518
9781601191953
1601191952
1861251009
9781861251008
ISSN1354-5116 ;
Physical Description1 online resource (xv, 478 pages) : illustrations

Cover

Table of Contents:
  • Contents
  • Series Introduction
  • Preface
  • Foreword
  • Part 1
  • Oxidation and Failure Mechanisms Under Cyclic Conditions
  • Interfacial Crack Growth During Temperature Changes
  • The Influence of Surface Pre-treatment on the Integrity of Alumina Scales on the ODS Alloy MA 956
  • The Effect of Water Vapour on the Oxidation of Alloys that Develop Alumina Scales for Protection
  • The Influence of Thermal Cycling on Internal Oxidation and Nitridation of Nickel-Base Alloys
  • Cyclic Oxidation of Thin FeCrAI(RE) Foils in Air: SEM and EPMA Investigations
  • Cyclic Oxidation of PM 1000Part 2
  • Test Procedures and Parameters Influencing Cyclic Oxidation Behaviour
  • Effect of Cycle Frequency on High-Temperature Oxidation Behaviour of Alumina- and Chromia-Forming Alloys
  • The Effect of Thermal Cycling on the Mechanical Failure of Alumina Scales formed on Commercial FeCrAI-RE Alloys
  • Cyclic Oxidation Testing and Modelling: a NASA Lewis Perspective
  • Significance of Experimental Procedures on the Hot Corrosion Behaviour of Nickel-Base Alloys under Cyclic Conditions
  • Advantages of Ferritic Stainless Steels in Cyclic High Temperature ConditionsInvestigation of a New Methodology in High Temperature Oxidation
  • Effect of Implanted Silicon on the Cyclic Oxidation Behaviour of AISI 304 and AISI 430 Stainless Steels
  • The Importance of Relevant Experimental Parameters for High Temperature Cyclic Oxidation Experiments
  • An attempt for a checklist
  • Corrosion of Heat Exchanger Steels in Cycled Gas Atmospheres at 600°C
  • Behaviour of Protective Coatings against Sulfidation under Cyclic Conditions
  • Part 3
  • Long Term Behaviour and Near-Service Conditions Long-Term, Cyclic Oxidation Behaviour of Three Chromia-Forming Alloys Exposed to Air at 982°C
  • Oxidation Limited Life of FeCrAI Based Alloys During Thermal Cycling
  • Characterisation of Oxidation Resistance of Heat-resistant Cast Alloys in the 5 x 24-h Test
  • Cyclic Oxidation Testing by Resistance Heating
  • Part 4
  • The Behaviour of Coatings Under Cycling Conditions
  • Thermal Cycling Testing of Thermal Barrier Coatings
  • Investigations of the Microstructure and Stress State in Oxide Scales
  • Numerically Calculated Oxidation Induced Stresses in Thermal Barrier Coatings on Cylindrical Substrates Electron Beam-Physical Vapour Deposited Thermal Barrier Coating Lifetime Response to Various Bond Coat Pre-treatments
  • Degradation of Aluminide, Chromium-Aluminide and Thermal Barrier Coatings in Conditions of Cyclic Thermal and Mechanical Loads
  • Thermal Cycling of NiAI Intermetallic Coatings Prepared by High Velocity Oxy-Fuel (HVOF) Thermal Spraying